高分子材料工程专业英语翻译1

《高分子材料工程专业英语翻译1》由会员分享，可在线阅读，更多相关《高分子材料工程专业英语翻译1（47页珍藏版）》请在装配图网上搜索。

1、Unit 1 What are polymers?What are polymers? For one thing, they are complex and giant molecules and are different from low molecular weight compounds like, say, common salt.什么是高聚物？首先，他们是合成物和大分子，而且不同于低分子化合物，譬如说普通的盐。To contrast the difference, the molecular weight of common salt is only 58.5, while th

2、at of a polymer can be as high as several hundred thousand, even more than thousand thousands.与低分子化合物不同的是，普通盐的分子量仅仅是58.5，而高聚物的分子量高于105，甚至大于106。These big molecules or macro-molecules are made up of much smaller molecules, can be of one or more chemical compounds.这些大分子或“高分子”由许多小分子组成。小分子相互结合形成大分子，大分子能够

3、是一种或多种化合物。To illustrate, imagine that a set of rings has the same size and is made of the same material. When these things are interlinked, the chain formed can be considered as representing a polymer from molecules of the same compound.举例说明，想象一组大小相同并由相同的材料制成的环。当这些环相互连接起来，可以把形成的链看成是具有同种化合物组成的高聚物。Alt

4、ernatively, individual rings could be of different sizes and materials, and interlinked to represent a polymer from molecules of different compounds.另一方面，环可以大小不同、材料不同, 相连接后形成具有不同化合物组成的聚合物。This interlinking of many units has given the polymer its name, poly meaning many and mer meaning part (in Greek

5、).聚合物的名称来自于许多单元相连接，poly意味着“多、聚、重复”，mer意味着“链节、基体”（希腊语中）。As an example, a gaseous compound called butadiene, with a molecular weight of 54, combines nearly 4000 times and gives a polymer known as polybutadiene (a synthetic rubber) with about 200 000molecular weight.例如：气态化合物丁二烯的分子量为54，连接4000次可得到分子量大约为2

6、00000的聚丁二烯（合成橡胶）高聚物。The low molecular weight compounds from which the polymers form are known as monomers. The picture is simply as follows:形成高聚物的低分子化合物称为单体。下面简单地描述一下形成过程：butadiene + butadiene + + butadiene-polybutadiene(4 000 time)丁二烯 丁二烯丁二烯聚丁二烯（4000次）One can thus see how a substance (monomer) with

7、 as small a molecule weight as 54 grow to become a giant molecule (polymer) of (544 000)200 000 molecular weight.能够知道分子量仅为54的小分子物质（单体）如何逐渐形成分子量为200000的大分子（高聚物）。It is essentially the “giantness” of the size of the polymer molecule that makes its behavior (different from that of a commonly known chemi

8、cal compound such as benzene.) 实质上正是由于聚合物的巨大分子尺寸才使其性能不同于像苯这样的一般化合物（的性能）Solid benzene, for instance, melts to become liquid benzene at 5.5 and , on further heating, boils into gaseous benzene.例如固态苯在5.5熔融成液态苯，进一步加热，煮沸成气态苯。As against this well-defined behavior of a simple chemical compound, a polymer l

9、ike polyethylene does not melt sharply at one particular temperature into clean liquid.与这类简单化合物明确的行为相比，像聚乙烯这样的聚合物不能在某一特定的温度快速地熔融成纯净的液体。Instead, it becomes increasingly softer and, ultimately, turns into a very viscous, tacky molten mass. Further heating of this hot, viscous, molten polymer does conv

10、ert it into various gases but it is no longer polyethylene. (Fig. 1.1) .而聚合物变得越来越软，最终变成十分粘稠的聚合物熔融体。将这种热而粘稠的聚合物熔融体进一步加热，它会转变成不同气体，但它不再是聚乙烯（如图1.1）Another striking difference with respect to the behavior of a polymer and that of a low molecular weight compound concerns the dissolution process.聚合物行为和低分子

11、量化合物另一不同的行为为溶解过程。 Let us take, for example, sodium chloride and add it slowly to fixed quantity of water. The salt, which represents a low molecular weight compound, dissolves in water up to a point (called saturation point) but, thereafter, any further quantity added does not go into solution but s

12、ettles at the bottom and just remains there as solid.例如，将氯化钠慢慢地添加到定量的水中。盐作为一种低分子量化合物，在水中溶解直到某一点（叫饱和点），但进一步添加, 盐不进入溶液中却沉到底部而保持原有的固体状态The viscosity of the saturated salt solution is not very much different from that of water. But if we take a polymer instead, say, polyvinyl alcohol, and add it to a fi

13、xed quantity of water, the polymer does not go into solution immediately.饱和盐溶液的粘度与水的粘度接近.但是，如果我们用聚合物，如聚乙烯醇添加到定量水中，聚合物不是马上进入到溶液中。 The globules of polyvinyl alcohol first absorb water, swell and get distorted in shape and after a long time go into solution. 聚乙烯醇颗粒首先吸水溶胀，发生变形，经过很长时间后，（聚乙烯醇分子）进入到溶液中。Als

14、o, we can add a very large quantity of the polymer to the same quantity of water without the saturation point ever being reached.同样地，我们可以将大量的聚合物加入到同样量的水中，不存在饱和点。As more and more quantity of polymer is added to water, the time taken for the dissolution of the polymer obviously increases and the mix u

15、ltimately assumes a soft, dough-like consistency.将越来越多的聚合物加入水中，认为聚合物溶解的时间明显地增加，最终呈现柔软像面团一样粘稠的混合物。Another peculiarity is that, in water, polyvinyl alcohol never retains its original powdery nature as the excess sodium chloride does in a saturated salt solution. 另一个特点是，在水中聚乙烯醇不会像过量的氯化钠在饱和盐溶液中那样能保持其初始的

16、粉末状态。In conclusion, we can say that (1) the long time taken by polyvinyl alcohol for dissolution, (2) the absence of a saturation point, and (3) the increase in the viscosity are all characteristics of a typical polymer being dissolved in a solvent and these characteristics are attributed mainly to

17、the large molecular size of the polymer.总之，我们可以讲（1）聚乙烯醇的溶解需要很长时间，（2）不存在饱和点，（3）粘度的增加是聚合物溶于溶液中的典型特性，这些特性主要归因于聚合物大分子的尺寸。The behavior of a low molecular weight compound and that of a polymer on dissolution are illustrated in Fig.1.2.总如图1.2说明了低分子量化合物和聚合物的溶解行为。Polymer: 高分子,聚合物.(repeat units)polymericpolym

18、erization“poly-”: 多的,聚合的. Polygon, 聚醚？聚酯？聚酰胺？聚乙烯？多官能团？polyfunctional “-mer”: part. Isomer, 同分异构体Macromolecule: 大分子,高分子Macro-: 大 （反义词？）Molecule, 分子 - Atom, 原子Molecular Weight, 分子量Micro-: 显微的。显微镜？Microscope. MicrosoftMonomer: 单体“mono-”: 单个 . Monocrystalline，monodisperse，monofunction“di-, bi-”: 双. “tri

19、-”: 三个. “tetra-”:四个Repeat Unit, 重复单元 - Monomer unit,单体单元Synthetic, 合成的, 如Synthetic RubberSynthesis, n, 合成 -Syntheses, vt, 合成Butadiene: 丁二烯。 Butyl-：丁基。-ene：烯。-yne：炔。乙烯？Ethylene . 1-丁烯？Butylene. 乙炔？Ethyne.Polyethylene: 聚乙烯. Ethyl-:乙基。 Ethylene: 乙烯。Ethane：乙烷 synthetic: 合成的。名词？动词？Viscous：粘的。名词？Plastics,

20、 塑料 - Rubber, 橡胶 - Fiber, 纤维Adhesive, 黏合剂 - Paints, 涂料Polybutadiene, 聚丁二烯Polyvinyl alcohol, 聚乙烯醇Polyvinyl chloride, 聚氯乙烯Polyester, 聚酯Polystyrene, 聚苯乙烯Polypropylene, 聚丙烯Polyethylene, 聚乙烯Polyamide, 聚酰胺Polyether:聚醚Thermoplastics, 热塑性塑料Thermosetting resin, 热固性树脂Elastomers, 弹性体Thermoelastomers, 热塑性弹性体Hom

21、opolymers and copolymers, 均聚物和共聚物Homo- ：均匀的。Homogenous:均相的 Hetero-：异的，不同的 heterogenous: 异相的Block copolymers,嵌段共聚物Random copolymers,无规共聚物Alternating copolymers,交替共聚物Terpolymers,三元共聚物Graft copolymers,接枝共聚物Polyvinyl alcohol: 聚乙烯醇。 Vinyl：乙烯基Sodium chloride, 氯化钠，potassium sulfate, 硫酸钾；sulfuric acid, 硫酸Se

22、ttle，使（液体）澄清，沉淀,沉降Precipitate, 使沉淀，使凝结Precipitant，沉淀剂Stir, 搅拌Saturation, 饱和 - Unsaturation, 不饱和Dissolution, n,溶解 -Dissolve, vt, 溶解solution n 溶液; solution polymerizationsolubility n 溶解度，溶解性solvent n 溶剂, solvent effectViscous, a, 粘稠的 -Viscosity, 粘度(性) Clean, 完全的，彻底的；sharply, 明显地，精明地，敏锐地，突然地，急剧地Increas

23、ingly, 越来越.，Striking, 显著的， 引人注目的，with respect to 关于，就而论Thereafter，此后Distort，畸变，扭变，变形。Consistency, 一致性，坚固性。Peculiarity, 独特性，特色，特质，特殊的东西，怪癖。issue from, 由.产生，由得出.Adventitious dventiSs,外来的，偶然的，abstract, 分离，转移profound,意义深远的，深刻的，notably，显著的，著名的，这个句型很有用 just as it is not necessary for to be , it is also no

24、t necessary for to be 正不一定是.一样， .也不一定是.The moment, 一.就.Segment, 链段Backbone, 主链，骨架(脊骨,脊柱)/skeleton, 骨骼,骨架（建筑）,骷髅Skeleton atom (structure),骨架原子（结构）substituent, substituted group,取代基side（pendant,lateral）group,侧基/end group,端基Side chain, 侧链，支链Side reaction, 副反应Linear polymers, 线型高分子/Nonlinear polymers,非线

25、型高分子Branched polymers,支化高分子Crosslinked polymers,交联高分子Stars and dendrimers,星型高分子及树枝状高分子Ladder polymers,梯型高分子Cyclolinear polymers,线型环聚合物/Cyclomatrix polymer,体型聚合物Telechelic polymers,远鳌聚合物，遥爪聚合物Mono-telechelic polymer,单遥爪聚合物Di-telechelic polymer,双遥爪聚合物Amorphous polymers,无定形高分子/Crystalline polymers,结晶高分

26、子Unit 2 Chain PolymerizationMany olefinic and vinyl unsaturated compounds are able to form chain-like macromolecules through elimination of the double bond, a phenomenon first recognized by Staudinger. Diolefins polymerize in the same manner, however, only one of the two double bonds is eliminated.S

27、taudinger首先发现许多烯烃和不饱和烯烃通过打开双键可以形成链式大分子。二烯烃以同样的方式聚合，但仅消除两个双键中的一个。 Such reactions occur through the initial addition of a monomer molecule to an initiator radical or an initiator ion, by which the active state is transferred from the initiator to the added monomer.这类反应是通过单体分子首先加成到引发剂自由基或引发剂离子上而进行的，靠这些

28、反应活性中心由引发剂转移到被加成的单体上。In the same way by means of a chain reaction, one monomer molecule after the other is added (200020000 monomers per second) until the active state is terminated through a different type of reaction.单体分子通过链式反应以同样的方式一个接一个地加上（每秒200020000个单体）直到活性中心通过不同的反应方式终止。The polymerization is a

29、 chain reaction in two ways: because of the reaction kinetic and because as a reaction product one obtains a chain molecule. The length of the chain molecule is proportional to the kinetic chain length.聚合反应成为链式反应的两种原因：反应动力学和作为链式反应产物分子。链分子的长度与动力学链长成正比。One can summarize the process as follow (R. is eq

30、ual to the initiator radical):链式反应可以概括为以下过程（R相当与引发剂自由基）：略One thus obtains polyvinylchloride from vinylchloride, or polystyrene from styrene, or polyethylene from ethylene, etc.因而通过上述过程由氯乙烯得到聚氯乙烯，或由苯乙烯获得聚苯乙烯，或乙烯获得聚乙烯，等等。The length of the chain molecules, measured by means of the degree of polymerizat

31、ion, can be varied over a large range through selection of suitable reaction conditions.分子链长通过聚合度测量，可以通过选择适宜的反应条件大为改变Usually, with commercially prepared and utilized polymers, the degree of polymerization lies in the range of 1000 to 5000, but in many cases it can be below 500 and over 10000.商业制备和使用

32、的聚合物，聚合度通常在10005000范围内，但在许多情况下可低于500或高于10000。This should not be interpreted to mean that all molecules of a certain polymeric material consist of 500, or 1000, or 5000 monomer units. In almost all cases, the polymeric material consists of a mixture of polymer molecules of different degrees of polyme

33、rization.这不应该把聚合物材料所有的分子理解为由500，或1000，或5000个单体单元组成。在几乎所有的情况下，聚合物材料由不同聚合度的聚合物分子的混合物组成。Polymerization, a chain reaction, occurs according to the same mechanism as the well-known chlorine-hydrogen reaction and the decomposition of phosegene.链式聚合反应的机理与众所周知的氯（气）-氢（气）反应和光气的分解机理相同。The initiation reaction,

34、which is the activation process of the double bond, can be brought about by heating, irradiation, ultrasonics, or initiators. The initiation of the chain reaction can be observed most clearly with radical or ionic initiators. 通过双键活化的引发剂反应，可以通过热、辐射、超声波或引发剂产生。可以很清楚地进行研究用自由基型或离子型引发剂引发的链式反应。These are en

35、ergy-rich compounds which can add suitable unsaturated compounds (monomers) and maintain the activated radical or ionic state so that further monomer molecules can be added in the same manner.这些是高能态的化合物，它们能够加成不饱和化合物（单体）并保持自由基或离子活性中心 以致单体可以以同样的方式进一步加成。For the individual steps of the growth reaction o

36、ne needs only a relatively small activation energy and therefore through a single activation step (the actual initiation reaction) a large number of olefin molecules are converted, as is implied by the term “chain reaction”.对于增长反应的各个步骤，每一步仅需要相当少的活化能，因此通过一步简单的活化反应（即引发反应）即可将许多烯类单体分子转化成聚合物，这正如连锁反应这个术语的

37、内涵那样。Because very small amounts of the initiator bring about the formation of a large amount of polymeric material (1:1000 to 1:1000), it is possible to regard polymerization from a superficial point of view as a catalytic reaction.因为少量的引发剂引发形成大量的聚合物原料（1：10001：10000），从表面上看聚合反应被看成是催化反应。For this reaso

38、n, the initiators used in polymerization reactions are often designated as polymerization catalysts, even though, in the strictest sense, they are not true catalysts because the polymerization initiator enters into the reaction as a real partner and can be found chemically bound in the reaction prod

39、uct ,i.e. ,the polymer.由于这个原因，通常把聚合反应的引发剂看作是聚合反应的引发剂。但因为聚合反应的催化剂进入到反应内部而成为一部分，同时可以在反应产物，既聚合物的末端发现催化剂，所以严格地讲它们不是真正意义上的催化剂，In addition to the ionic and radical initiators there are now metal complex initiators (which can be obtained, for example, by the reaction of titanium tetrachloride or titanium t

40、richloride with aluminum alkyls), which play an important role in polymerization reactions (Ziegler catalysts) ,The mechanism of their catalytic action is not yet completely clear.除离子引发剂和自由基引发剂外，还有金属络合物引发剂（可以通过四氯化钛或三氯化钛与烷基铝的反应得到）。它们在聚合反应中起到了重要作用（齐格纳引发剂）。它们催化活动的机理还不是十分清楚。Radical, 自由基； ion, 离子， ionic，

41、 离子的，ionic polymer， 离子聚合物， ionomer，离聚体Activation, 活化（作用），活化过程; Active state， 活性中心Polyvinyl chloride: 聚氯乙烯Polystyrene : 聚苯乙烯Degree of polymerization: 聚合度（DP)Mechanism:机理Chlorine：氯气;Hydrogen: 氢气Decomposition：分解。Degradation: 降解Irradiation,辐射，照射。ultrasonics, 超声波Imply, 暗指，含有.的意思 regard, 把.看作.Catalyst: 催化

42、剂Ionic：离子的 。 Ion: 离子。Cation: 阳离子。Anion:阴离子Complex：络合物Di-: 二。Tri-:三。Tetra-: 四。Mono-：单。Penta-：五个；hexa-:六Alkyl：烷基 alkane：烷烃。Alkene: 烯烃by means of: By usingOneafter the other 一个接一个.be proportional to: 和成正比Lie in 处于，落在，在于Bring about,引起，产生，导致from a superficial point of view, 从表面上看in the proper(strict、lite

43、ral)sense 在本来（严格、字面）的意义上说的play an important role in: 在.方面起重要作用Even though=even if ,即使，纵然In addition to 除了.之外，在.起重要作用Radical,自由基/Initiator,引发剂/ Unsaturated monomer, 不饱和单体Organic peroxide, 有机过氧化物/hydroperoxide, 过氧化氢Redox agent, 氧化还原试剂Azo compounds,偶氮化合物Organometallic reagents,有机金属Irradiation,光辐射，紫外光照射

44、High energy radiation, 高能辐射Homolytic dissociation, 均裂Chain initiation, 链引发反应/chain propagation,链增长反应Steady-state assumption,稳态假设Rate of polymerization,聚合速率Chaintransfer,链转移/chain termination ，链终止反应Combination, 偶合（终止），结合Disproportionation,歧化（终止）UNIT 3 Step-Growth polymerizationMany different chemical

45、 reactions may be used to synthesize polymeric materials by step-growth polymerization. These include esterification, amidation, the formation of urethanes, aromatic substitution, etc.通过逐步聚合可用许多不同的化学反应来合成聚合材料。这些反应包括酯化、酰胺化、氨基甲酸酯、芳香族取代物的形成等。Polymerization proceeds by the reactions between two differen

46、t functional groups, e.g., hydroxyl and carboxyl groups, or isocyanate and hydroxyl groups.通过在两种不同的官能团，如，羟基和羧基，或异氰酸酯和羟基之间可发生聚合反应。All step-growth polymerization fall into two groups depending on the type of monomer(s) employed. The first involves two different polyfunctional monomers in which each mo

47、nomer possesses only one type of functional group.所有的逐步聚合反应根据所使用单体的类型可分为两类。第一类涉及两种不同的官能团单体，每一种单体仅具有一种官能团。A polyfunctional monomer is one with two or more functional groups per molecule. The second involves a single monomer containing both types of functional groups.一种多官能团单体每个分子有两个或多个官能团。第二类涉及含有两类官能团

48、的单个单体。The synthesis of polyamides illustrates both groups of polymerization reactions. Thus, polyamides can be obtained from the reaction of diamines with diacids or from the reaction of amino acids with themselves. 聚酰胺的合成说明了两类聚合反应。因此聚酰胺可以由二元胺和二元酸的反应或氨基酸之间的反应得到。The two groups of reactions can be rep

49、resented in a general manner by the equations as follows 两种官能团之间的反应一般来说可以通过下列反应式表示Reaction (3.1) illustrates the former, while (3.2) is of the latter type.反应（3.1）说明前一种形式，而反应（3.2）具有后一种形式。Polyesterification, whether between diol and dibasic acid or intermolecularly between hydroxy acid molecules, is a

50、n example of a step-growth polymerization process.聚酯化反应是逐步聚合反应过程的一个例子。反应可能在二元酸和二元醇之间或羟基酸分子间进行。The esterification reaction occurs anywhere in the monomer matrix where two monomer molecules collide, and once the ester has formed, it, too, can react further by virtue of its still-reactive hydroxyl or c

51、arboxyl groups. 酯化反应出现在单体本体中两个单体分子相碰撞的位置，且酯一旦形成，依靠酯上仍有活性的羟基或羧基还可以进一步进行反应。The net effect of this is that monomer molecules are consumed rapidly without any large increase in molecular weight.酯化的结果是单体分子很快地被消耗掉，而分子量却没有多少增加。Fig. 3.1 illustrates this phenomenon. Assume, for example, that each square in F

52、ig. 3.1a represents a molecule of hydroxy acid. After the initial dimmer molecules from (b), half the monomer molecules have been consumed and the average degree of polymerization (DP) of polymeric species is 2.图3.1说明了这个现象。假定图3.1中的每一个方格代表一个羟基酸分子。产生二聚体分子后（b），一半的单体分子消耗了，这时平均聚合度（DP）是2。As trimer and mor

53、e dimer molecules form (c), more than 80% of the monomer molecules have reacted, but DP is still 2.5. When all the monomer molecules have reacted (d), DP is 4.（c）中形成三聚体和更多的二聚体，超过80%的单体分子已参加反应，但DP仅仅还是2.5。（d）中所有的单体反应完，DP是4。But each polymer molecule that forms still has reactive end groups; hence the p

54、olymerization reaction will continue in a stepwise fashion, with each esterification step being identical in rate and mechanism to the initial esterification of monomers.但形成的每一种聚合物分子还有反应活性的端基；因此，聚合反应将以逐步的方式继续进行，其每一步酯化反应的反应速率和反应机理均与初始单体的酯化作用相同。Thus, molecular weight increases slowly even at high leve

55、ls of monomer conversion, and it will continue to increase until the viscosity build-up makes it mechanically too difficult to remove water of esterification or for reactive end groups to find each other.这样，分子量在高单体转化率下缓慢增加，继续增加直到粘度增加到难以除去酯化反应的水或端基难以相互反应为止。It can also be shown that in the A-A+B-B typ

56、e of polymerization, an exact stoichiometric balance is necessary to achieve high molecular weights. If some monofunctional impurity is present, its reaction will limit the molecular weight by rendering a chain end inactive.在A-A+B-B的聚合反应中，精确的定量配比是获得高分子量所必需的。假如存在一些单官能团杂质，由于链的端基失活，其反应将限制分子量。Similarly,

57、 high-purity monomers are necessary in the A-B type of polycondensation and it follows that high-yield reactions are the only practical ones for polymer formation, since side reactions will upset the stoichiometric balance.同样，在A-B类的缩聚反应中高纯度的单体是必要的。因为副反应会破坏定量配比，能形成聚合物的实用方法只能是高收率的反应。Step-growth polyme

58、rization: 逐步聚合(包括缩聚)Synthesize : v. 合成 synthesis: n.Esterification: 酯化(COOH 和-OH的反应). Ester: 酯. COOR polyester, 聚酯。Amide: 酰胺 (-CONH2) ， Amidation: 酰胺化，polyamide, 聚酰胺，尼龙Urethane: (cabarmate)氨基甲酸酯 . RO(CO) NR2. 氨基甲酸乙酯，NH2CO2C2H5Polyurethane, 聚氨酯， 弹性体。Aromatic: 芳香族的 (环状的闭合共轭体系,如含苯环的化合物)Aromatic, 芳香族的，a

59、romatics，芳香族化合物，香料，芳香剂。aroma, 香味，aromatic acid, 芳香酸Substitution: n.取代,代替,取代反应 substitute: v. 取代举例: C6H5-Br C6H5-OH Functional group: 官能团 Monofunctional, 单官能度的/difunctional,两官能团的Polyfunctional, 多官能团的，多官能度的Hydroxyl，羟基，hydro-，氢化的，氢的，水的；-oxyl，氧基，如methoxyl，甲氧基。carboxyl， 羧基，carbo-，碳，羰isocyanate，异氰酸酯。RN=C=

60、O. iso-，异，等位，如，isoelectric point，等电离点。Isobutylene，异丁烯。 Iso-propanol : 异丙醇。异丁醇ROH + RNCO ROC(O)N(H)R Cyanate, 氰酸盐，氰酸酯, RO-CN。Cyanide, 氰化物，如potassium cyanate, 氰化钾。Dimmer, 二聚体，trimer，三聚体，tetramer，四聚体，pentamer，五聚体，Hexamer，六聚体。Heptamer, 七聚体，Oligomer,低聚物，低聚体 Diamine，二元胺/ diol,二元醇/ triol, 三元醇/ polyol,多元醇酸

61、Ethylene diamine(?)dibasic,二元的/ diacid, 二元酸/ amino acid，氨基酸Fall into, 归入，可分为.Depending on, 根据.In a general manner, 一般来说Whether.or., 无论是.还是., 或者或者，不是就是.By（后in）virtue of.依靠，借助于.Be identical in to, 在.方面和.是相同的。Identicalaidentikl, a, 同一的，完全相同的，相等的，有同一原因（来源）的，Identical twins, 同卵双胞胎，identical equation, 恒等式

62、The fingerprints of no two persons are identical. Your voice is identical to hers in volume.build-up: 增加烷(-ane) methane ethane propane butane 烷基（-yl) methyl ethyl propyl butyl 亚烷基(-ylene) methylene ethylene 环烷(cyclo-) cyclopropane cyclohexane 烯(-ene) ethene propene butene 炔(-yne) ethyne propyne buty

63、ne 醇(-ol) methanol ethanol propanol butanol 醛(-al) formaldehyde ethanal 酮(-one) acetone 酸(-ic acid) acetic acid酸酐(anhydride) formic anhd. acetic anhd. 酰胺 (amide) acetamide 胺(amine) methyl amine ethyl aminestoichiometric balance，化学计量平衡/conversion,转化率/yield,产率The average degree of polymerization, 平均聚合度Molecular weight:分子量Impurity：杂质。Purity: 纯度。Im-:不。 impossiblePolycondensation: 缩聚Side reaction: 副反应UNIT 4 Ionic PolymerizationIonic polymerization, similar to radical polymerization, also has the mechanism of a chain reac